d a t a sh eet product speci?cation supersedes data of november 1997 file under ferrite ceramics, ma01 1999 dec 23 ferrite ceramics e22/6/16/r planar e cores
1999 dec 23 2 philips components product speci?cation planar e cores e22/6/16/r cores effective core parameters of an e/plt combination ordering information for plates symbol parameter value unit s (i/a) core factor (c1) 0.324 mm - 1 v e effective volume 2100 mm 3 i e effective length 26.1 mm a e effective area 80.4 mm 2 a min minimum area 72.6 mm 2 m mass of e core half ? 6.5 g m mass of plate ? 4g grade type number 3c90 plt22/16/2.5/s-3c90 3c94 plt22/16/2.5/s-3c94 3c96 plt22/16/2.5/s-3c96 3f3 plt22/16/2.5/s-3f3 3f35 plt22/16/2.5/s-3f35 3f4 plt22/16/2.5/s-3f4 3e6 plt22/16/2.5/s-3e6 a ndbook, halfpage cbw177 21.8 0.4 16.8 0.4 3.2 0.1 15.8 0.3 5.7 0.1 5 0.1 2.8 + 0.2 0 4.7 0.15 fig.1 e22/6/16/r. dimensions in mm. n dbook, halfpage cbw178 21.8 0.4 15.8 0.3 2.9 0.05 2.5 0.1 2.9 + 0.2 0 fig.2 plt22/16/2.5/s. dimensions in mm.
1999 dec 23 3 philips components product speci?cation planar e cores e22/6/16/r core halves for use in combination with a slotted plate (plt/s) a l measured in combination with a slotted plate (plt/s) clamping force for a l measurements, 20 10 n; measurement coil as for e22/6/16. grade a l (nh) m e air gap ( m m) type number 3c90 160 3% ? 42 ? 950 e22/6/r-3c90-a160-p 250 3% ? 66 ? 550 e22/6/r-3c90-a250-p 315 3% ? 83 ? 400 e22/6/r-3c90-a315-p 400 5% ? 106 ? 280 e22/6/r-3c90-a400-p 630 8% ? 166 ? 160 e22/6/r-3c90-a630-p 6150 25% ? 1620 ? 0 e22/6/16/r-3c90 3c94 160 3% ? 42 ? 950 e22/6/r-3c94-a160-p 250 3% ? 66 ? 550 e22/6/r-3c94-a250-p 315 3% ? 83 ? 400 e22/6/r-3c94-a315-p 400 5% ? 106 ? 280 e22/6/r-3c94-a400-p 630 8% ? 166 ? 160 e22/6/r-3c94-a630-p 6150 25% ? 1620 ? 0 e22/6/16/r-3c94 3c96 5450 25% ? 1440 ? 0 e22/6/16/r-3c96 3f3 160 3% ? 42 ? 950 e22/6/r-3f3-a160-p 250 3% ? 66 ? 550 e22/6/r-3f3-a250-p 315 3% ? 83 ? 400 e22/6/r-3f3-a315-p 400 5% ? 106 ? 280 e22/6/r-3f3-a400-p 630 8% ? 166 ? 160 e22/6/r-3f3-a630-p 5000 25% ? 1320 ? 0 e22/6/16/r-3f3 3f35 4100 25% ? 1080 ? 0 e22/6/16/r-3f35 3f4 160 3% ? 42 ? 950 e22/6/r-3f4-a160-p 250 3% ? 66 ? 550 e22/6/r-3f4-a250-p 315 3% ? 83 ? 400 e22/6/r-3f4-a315-p 400 5% ? 106 ? 280 e22/6/r-3f4-a400-p 630 8% ? 166 ? 160 e22/6/r-3f4-a630-p 2900 25% ? 770 ? 0 e22/6/16/r-3f4 3e6 26000 +40/ - 30% ? 6900 ? 0 e22/6/16/r-3e6
1999 dec 23 4 philips components product speci?cation planar e cores e22/6/16/r properties of core sets under power conditions properties of core sets under power conditions (continued) grade b (mt) at core loss (w) at h = 250 a/m; f = 10 khz; t = 100 c f = 100 khz; = 100 mt; t = 100 c f = 100 khz; = 200 mt; t = 100 c f = 400 khz; =50mt; t = 100 c e18/r+plt18/s-3c90 3 320 0.235 -- e18/r+plt18/s-3c94 3 320 0.180 ? 0.88 ? 0.39 e18/r+plt18/s-3c96 3 320 ? 0.13 ? 0.62 ? 0.28 e18/r+plt18/s-3f3 3 300 0.230 - 0.40 e18/r+plt18/s-3f35 3 300 0.230 -? 0.20 e18/r+plt18/s-3f4 3 250 --- grade b (mt) at core loss (w) at h = 250 a/m; f = 10 khz; t = 100 c f = 500 khz; = 50 mt; t = 100 c f = 500 khz; = 100 mt; t = 100 c f=1mhz; =30mt; t = 100 c f = 3 mhz; = 10 mt; t = 100 c e18/r+plt18/s-3c90 3 320 ---- e18/r+plt18/s-3c94 3 320 ---- e18/r+plt18/s-3c96 3 320 ---- e18/r+plt18/s-3f3 3 300 ---- e18/r+plt18/s-3f35 3 300 ? 0.34 ? 2.50 -- e18/r+plt18/s-3f4 3 250 -- 0.41 0.66 b ? b ? b ? b ? b ? b ? b ?
1999 dec 23 5 philips components product speci?cation planar e cores e22/6/16/r mounting parts general data and ordering information item material figure type number clamp stainless steel (crni) 3 clm-e22/plt22 fig.3 clamp for e22/r+plt22/s. dimensions in mm. handbook, halfpage 9 2.5 21.4 22.2 0.3 cbw179 8.7 0.1 0.4 o lumns 5.25 min. 16.2 max. 22.4 min. 25.8 min. 2.8 min. 16.3 min. r 0.8 max. cbw554 fig.4 recommended pcb cut-out for clamped cores. dimensions in mm.
|